Please refer to the explanation of product's characteristics when ordering.
Alloy Property
High level of resistance to corrosion and welding, Middle level of strength, Relatively high level of cold working property
Basic Property
| (%) |
Si |
Fe |
Cu |
Mu |
Mg |
Cr |
Zn |
Ti |
Al |
| Max |
0.800 |
0.700 |
0.400 |
0.150 |
1.200 |
0.350 |
0.250 |
0.150 |
|
| Min |
0.400 |
|
0.150 |
|
0.800 |
0.040 |
|
|
|
| Actual |
0.45 |
0.573 |
0.177 |
0.095 |
0.875 |
0.128 |
0.0091 |
0.021 |
97.61 |
Mechanical Property of AL6061
| Tensile Strength N/㎟ (kgf/㎟) |
Proof Stress N/㎟ (kgf/㎟) |
Elongation % |
| 310 |
230 |
25 |
Major Usage
Optical equipments for transporting structural materials like vehicle, ship and others, ordinary structural materials and mechanical parts
Basic Property
| Mark |
Definition |
Application |
| T21 |
Completely processed with annealing |
|
| T3 |
Cold working processed after solution treatment |
Applied to products with cold working done to increase the strength OR
products with improved mechanical property with cold working effects
|
| T36 |
6% of cold working processed after solution treatment |
Applied to products with cold working done after solution treatment |
| T4 |
Natural aging done after solution treatment |
Applied to products with their effects of cold working after solution treatement not verified |
| T42 |
Natural aging done after solution treatment |
Applied to products with completely stable state due to natural aging after solution treatment |
| T5 |
Artificial aging done after sudden cold working after processing in high temperature |
Applied to products with artificial aging done to improve their mechanical propertied or stable their measurement after sudden cold working after processing in high temperature |
| T6 |
Artificial aging done after solution treatment |
Applied to products requiring improved strength with no cold working after solution treatment |
| T61 |
Artificial aging with hot water injected after solution treatment |
Applied to products with no cold working after solution treatment OR with their effects of cold working after solution treatment not verified |
| T62 |
Artificial aging done after solution treatment |
Applied to products whose elongation is emphasized after solution treamtnet |
| T8 |
Artificial aging done with cold working after solution treatment |
Applied to products with cold working done to increase the strength OR products with improved cold working effects |
| T83 |
Artificial aging done with 3% of cold working after solution treatment |
|